COATING TYPE: NO-VOC ACRYLIC COPOLYMER
NO-VOC: Waterborne latex single component acrylic-vinyl-rubber copolymer with no measurable EPA V.O.C. Possesses similar properties to Thermalbond systems and may be used in areas where zero (0) emission is required.
MIXING RATIO: N/A
POT LIFE: N/A
PUMP PRESSURE: 1200-1500 PSI
TIP SIZES: 6/17,6/19,6/21
FILTERS: 60 MESH
MIN STEEL TEMP: 50 DEG F
MIN APPLICATION TEMP: 50 DEG F
MIN RELATIVE HUMIDITY: *
REQUIRED WET MILS: 10-12
SPRAY TECHNIQUE: CROSSCOAT 30% OVERLAP
DRY TO TOUCH: 1-2 HRS
MIN RECOAT TIME: DRY TO TOUCH
EQUIPMENT REQUIREMENTS: AIRLESS
V.O.C.: 0.00
SUBSTRATE: Ferros/Non-Ferros metals
SURFACE PREP: SSPC-SP-6/PRIME
POT LIFE: N/A
PUMP PRESSURE: 1200-1500 PSI
TIP SIZES: 6/17,6/19,6/21
FILTERS: 60 MESH
MIN STEEL TEMP: 50 DEG F
MIN APPLICATION TEMP: 50 DEG F
MIN RELATIVE HUMIDITY: *
REQUIRED WET MILS: 10-12
SPRAY TECHNIQUE: CROSSCOAT 30% OVERLAP
DRY TO TOUCH: 1-2 HRS
MIN RECOAT TIME: DRY TO TOUCH
EQUIPMENT REQUIREMENTS: AIRLESS
V.O.C.: 0.00
SUBSTRATE: Ferros/Non-Ferros metals
SURFACE PREP: SSPC-SP-6/PRIME
SWEAT IN TIME: N/A
THINNING: N/A
SOLVENT TYPE: WATER
REDUCTION: NONE
VISCOSITY: 3500-5500 CPS
MAX STEEL TEMP: 85 DEG F
MAX APPLICATION TEMP: 85 F
MAX RELATIVE HUMIDITY: *
REQUIRED DRY MILS: 5.5-6.6
DRY THROUGH: 8-10 HRS
MAX RECOAT TIME: WILL NOT LIFT
SOLIDS BY VOLUME: 50-55%
FREEZE THAW: NONE
D.O.T.: NON-FLAMMABLE
THINNING: N/A
SOLVENT TYPE: WATER
REDUCTION: NONE
VISCOSITY: 3500-5500 CPS
MAX STEEL TEMP: 85 DEG F
MAX APPLICATION TEMP: 85 F
MAX RELATIVE HUMIDITY: *
REQUIRED DRY MILS: 5.5-6.6
DRY THROUGH: 8-10 HRS
MAX RECOAT TIME: WILL NOT LIFT
SOLIDS BY VOLUME: 50-55%
FREEZE THAW: NONE
D.O.T.: NON-FLAMMABLE