COATING TYPE: AQUATHANE-WATERBORNE URETHANE SINGLE & TWO-COMPONENT
AQUATHANE: Water dispersion single or two-component urethane – copolymers with dehydrated V.O.C. range of 1.6-2.4; must be used with Aqua-Epoxy for optimum results.
MIXING RATIO: 9:1
POT LIFE: 8-10hrs
PUMP PRESSURE: 1200-1500 PSI
TIP SIZES: 6/15
FILTERS: 60 MESH
MIN STEEL TEMP: 40 DEG F
MIN APPLICATION TEMP: 40 DEG F
MIN RELATIVE HUMIDITY: SEE *
REQUIRED WET MILS: 4-6
SPRAY TECHNIQUE: CROSSCOAT 50% OVERLAP
DRY TO TOUCH: 30-60 MIN
EQUIPMENT REQUIREMENTS: AIRLESS/AIR
V.O.C.: 1.6-2.4 DEHYDRATED
SUBSTRATE PREP: CRS, HRS
D.O.T.: NON-FLAMMABLE
POT LIFE: 8-10hrs
PUMP PRESSURE: 1200-1500 PSI
TIP SIZES: 6/15
FILTERS: 60 MESH
MIN STEEL TEMP: 40 DEG F
MIN APPLICATION TEMP: 40 DEG F
MIN RELATIVE HUMIDITY: SEE *
REQUIRED WET MILS: 4-6
SPRAY TECHNIQUE: CROSSCOAT 50% OVERLAP
DRY TO TOUCH: 30-60 MIN
EQUIPMENT REQUIREMENTS: AIRLESS/AIR
V.O.C.: 1.6-2.4 DEHYDRATED
SUBSTRATE PREP: CRS, HRS
D.O.T.: NON-FLAMMABLE
SWEAT IN TIME: N/A
THINNING: 20-30%
SOLVENT TYPE: WATER
REDUCTION: NONE
VISCOSITY: 3500-5500 CPS
MAX STEEL TEMP: 85 DEG F
MAX APPLICATION TEMP: 85 DEG F
MAX RELATIVE HUMIDITY: SEE *
REQUIRED DRY MILS: 2.0-3.0
DRY THROUGH: 8-10 HRS.
MAX RECOAT TIME: WILL NOT LIFT
SOLIDS BY VOLUME: 60-65%
FREEZE THAW: NONE
SURFACE PREP: PRIMED WITH AQUA-EPOXY
THINNING: 20-30%
SOLVENT TYPE: WATER
REDUCTION: NONE
VISCOSITY: 3500-5500 CPS
MAX STEEL TEMP: 85 DEG F
MAX APPLICATION TEMP: 85 DEG F
MAX RELATIVE HUMIDITY: SEE *
REQUIRED DRY MILS: 2.0-3.0
DRY THROUGH: 8-10 HRS.
MAX RECOAT TIME: WILL NOT LIFT
SOLIDS BY VOLUME: 60-65%
FREEZE THAW: NONE
SURFACE PREP: PRIMED WITH AQUA-EPOXY